Product Description
SAE 4140 EN19 42CRMO4 DIN 1.7225 FORGED Round Steel Bar
1.42crmo forged steel bar sizes we can offer;
Round bar: 200-1000mm
Square bar:150×150-600×600mm
2.Supply condition for 4140 Forged steel bars:Black /Rough Machined /Rough turned
3.Futhur heat treatment for 4140 forged steel :
Normalized
Annealed
Q&T(Quenched&Tempered)
4.4140 Forged Steel round bar tolerance:
Black surface
Forged sizes up to 500mm (-0/+5mm)
Forged sizes above 500mm in diameter (-0/+8mm)
Machined surface to all sizes (-0/+3mm)
5.42crmo Steel Equivalent
| Standard | AISI / SAE 4140 |
| UNS | - |
| WERKSTOFF NR. | 41CrMo4, 42CrMo4, 42CrMoS4, 43CrMo4 |
| BS 970 | 708M40, 708A42, 709M40, En19, En19C |
| UNI | 41CrMo4, 38CrMo4 (KB), G40 CrMo4, 42CrMo4 |
| JIS | SCM 440, SCM 440H, SNB 7, SCM 4M, SCM 4 |
| EN name | 42CrMo4 |
| EN # | 1.7223, 1.7225, 1.7227, 1.3563 |
6.4140 Forged steel chemical composition
| Standard | Grade | C | Si | Mn | P | S | Cr | Mo |
| ASTM A29 | 4140 | 0.38-0.43 | 0.15-0.35 | 0.75-1.00 | ≤ 0.035 | ≤ 0.04 | 0.8-1.1 | 0.15-0.25 |
| 42CrMo4 | 0.38-0.45 | ≤ 0.4 | 0.6-0.90 | ≤ 0.025 | ≤ 0.035 | 0.9-1.2 | 0.15-0.30 | |
| EN10083 | 1.7225 | |||||||
| JIS G4105 | SCM440 | 0.38-0.43 | 0.15-0.35 | 0.6-0.85 | ≤ 0.035 | ≤ 0.04 | 0.9-1.2 | 0.15-0.30 |
| GB 3077 | 42CrMo | 0.38-0.45 | 0.17-0.37 | 0.5-0.80 | ≤ 0.035 | ≤ 0.035 | 0.9-1.2 | 0.15-0.25 |
| BS 970 | EN19 | 0.35-0.45 | 0.15-0.35 | 0.5-0.80 | ≤ 0.035 | ≤ 0.035 | 0.9-1.5 | 0.2-0.40 |
7.4140Steel Application
4140 steel finds many applications as forgings for the aerospace,oil and gas,automotive, agricultural and defense industries etc.
Typical applications for 4140 steel uses include:forged gears,spindles,fixtures,jigs,collars,Axles,conveyor parts,crow bars,logging parts,shafts,sprockets,studs,pinions,pump shafts, rams, and ring gears etc
8.Quality control:
1. Melting Process: EAF/BOF+LF+VD resulting in ingots
2. Both ends cut by saw
3. Ratio of forging:minimum 3:1
4. Grain size of final product: according to ASTM E112 more than 5,preferred more than 8
5. Ultrasonic test: As per SEP1921 Class C/c or D/d
9.Heat treatment of 4140 Steel
Quenched and Tempered (+QT) of EN19 Steel
1. Heat 42crmo steel slowly to 840-875°C;
2. Soak at this temperature then quench in oil;
3. Temper as soon as 42crmo reach room temperature (20°C);
4. Heat uniformly to the suitable temperature of 560°C;
5. Withdraw the material from the furnace and cool in the air.
Annealing of 42crmo Alloy Steel
1. Heat the 42crmoslowly to 800-850°C and allow enough time.
2. Cool slowly in the furnace to 480°C followed by air cooling
10.MOQ: one piece per size/grade
11.Payment term: FOB CIF CFR EXW and so on
12.Delivery time : 7 to 30 days after deposit received.