Product Description
1.Equivalent Steel Grade to 42CrMo4
QUALITY | EUROPE | GERMANY | FRANCE | SPAIN | G.B. | USA | |
EN | DIN | W.n. | AFNOR | UNE | B.S. | AISI/SAE | |
42CrMo4 | 42CrMo4 | 42CrMo4 | 1.7225 | 42CD4 | F1252 | 708M40 | 4140 |
2.42CrMo4 Steel Chemical composition
42CrMo4/1.7225 | C | Mn | Si | P | S | Cr | Mo |
0.38-0.45 | 0.60-0.90 | 0.40 max | 0.035 max | 0.035 max | 0.90-1.20 | 0.15-0.30 |
3.Mechanical property of 42CrMo4 according to EN10083-3
(Property canbe adjusted by changing heat treatment tempreture )
d ≤ 16mm | ||||
Re min | Rm | A min | Z min | KVb min |
N/mm2 | % | % | J | |
900 | 1100 - 1300 | 10 | 40 | - |
16mm < d ≤ 40mm | ||||
Re min | Rm | A min | Z min | KVb min |
N/mm2 | % | % | J | |
750 | 1000-1200 | 11 | 45 | 35 |
40mm < d ≤ 100mm | ||||
Re min | Rm | A min | Z min | KVb min |
N/mm2 | % | % | J | |
650 | 900 -1100 | 12 | 50 | 35 |
100mm < d ≤ 160mm | ||||
Re min | Rm | A min | Z min | KVb min |
N/mm2 | % | % | J | |
550 | 800 -950 | 13 | 50 | 35 |
160mm < d ≤ 250mm | ||||
Re min | Rm | A min | Z min | KVb min |
N/mm2 | % | % | J | |
500 | 750-900 | 14 | 55 | 35 |
4.Heat Treatment of 42CrMo4 Steels
Annealing of 42CrMo4 Steels
- Heat steel 42CrMo4 forged steel slowly and thoroughly to 800-850°C;
- Cool slowly in the furnace to the temperature 480°;
- Complete annealing the steel in the air.
Quenched and Tempered (Q+T)
- Heat 42CrMo4 steel slowly to 880°C;
- Soak at this temperature then quench in oil;
- Temper as soon as 42CrMo4 steel reach room temperature (20°C);
- Heat uniformly to the suitable temperature of 560°C;
- Withdraw the 42CrMo4 material from the furnace and cool in the air.
42CrMo4 alloy steel is widely used for engineering steel purpose, such as: making various kinds of machinery, automobile, mining spare part, the gearwheel of the engine, the driving gear of supercharger, the connecting rob, the pinchock under the high pressure, parts for power train applications, cold formed fastener components, shafts, gears, drill collars for the oil exploration, etc.
6.Quality control:
1. Melting Process: EAF+LF+VD
2. Both ends cut by saw
3. Ratio of forging:minimum 3:1
4. Grain size of final product: according to ASTM E112 more than 5,preferred more than 8
5. Ultrasonic test: As per SEP1921 Class C/c or D/d